Study material for textile engineering service? Previous years solved question papers?


dear sir

i am preparing for combined engineering service exam,i choosed textile engineering subject.so i need study material for textile engineering service and also need upto date previous solved question paper.

kindly send your reply.

regards
j.birla





Related Questions:
  1. Textile Engineering objective type question papers (solved) and study material
  2. Study material and notes along with last 10 years solved question papers of AMIE Section A?
  3. Study material and solved question papers of previous years for the post of security assistant?
  4. Study material and previous years solved question papers of RRB Secunderabad? -- [Most Discussed]
  5. Previous years solved question papers of engineering service exam in mechanical department?
  6. CEED study material and previous solved question papers with answers
  7. Any institute or coaching centre in India which provides postal study material? Solved previous years question papers for Social Work Paper 2 and 3 of UGC NET exam?
  8. Which study material should I refer for GATE Civil Engineering? Last 10 years question papers of the GATE exam for Civil Engineering Students?
  9. Study material for APPSC AE post? Previous years solved papers of APPSC AE post exam? Is there negative marking in the exam?
  10. ARS Textile Engineering Previous Years Question Papers?
  11. Previous year solved question papers of NET exam? Study material for the same?
  12. Where can I download study material for AFCAT Exam? Best Books to prepare for this Exam? Previous year Question Papers for this Exam?
  13. How may I get SBI PO exam solved question papers? How to get study materials for the same
  14. Previous 12 years solved question papers of Mathematics for Assistant Director of Hand loom and Textile post -- [New]
  15. Study material and previous years question papers for RPF inspector prosecution?
  16. Where to get study material for MCA entrance exam? Previous years question papers?
  17. Study material for CMPDI Jr Scientific Assistant Grade II? Solved question papers of last years?
  18. Study material for GATE in ECE? Previous years question papers?
  #2  
9th August 2011, 07:00 PM
excuse me
 
Join Date: May 2011
Posts: 50
Thumbs up Re: Study material for textile engineering service? Previous years solved question papers?

I am telling you the website which can satisfy most of the queries


http://www.onestopgate.com/gate-study-material/textile/

If you need any further assistance then reply on this very post.

I have replied what i understood from your question.


With regards
Varun singh
  #3  
20th October 2011, 06:15 PM
Unregistered
Guest
 
Posts: n/a
Default Re: Study material for textile engineering service? Previous years solved question papers?

want model question paper for tf
  #4  
21st January 2013, 07:24 PM
Unregistered
Guest
 
Posts: n/a
Default Re: Study material for textile engineering service? Previous years solved question papers?

want model question paper for Asst engg(electrical)pwd
Reply With Quote
  #5  
15th January 2014, 09:28 PM
jpnbiswal
Junior Member
 
Join Date: Dec 2013
Posts: 9
Default Re: Study material for textile engineering service? Previous years solved question papers?

PART 10 - TEXTILE TECHNOLOGY
(Answer ALL questions)
76. The tensile strength of polynosic fibre is
around
1. 3 to 3.5 gmsldenier
3. to gmsldenier
77. In viscose solution preparation xanthation
process takes normally from
1. 10 minutes
60 to 180 minutes
3. 5 hours
4. 24 hours
78. The temperature of molten polymer in nylon
81.
82.
The tenacity range of acrylic fibre in
gmsldenier is
1. to 1.2
The modern false twist texturizing machines
can impart false twist in to moving yarn a t
the rate of
1. six million RPM
2. 1 2 million RPM
3. only 30,000 RPM
4. RPM only
66 manufacture is around
79. In acrylic fibre manufacture, the polymer
concentration ranges from
83. High bulk yarns are produced from
1. relaxed fibres
2. unrelaxed fibres
3. a blend of relaxed and unrelaxed fibres
filaments
84. The cord fabrics used in conveying belt
applications approximately weigh
4. 70 to 8 0 %
80. The work factor of viscose staple fibre is
around
85. The cotton cloth construction normally
applied in V-belts in and
is
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
86. The standard
parachute cloth in
1. 2 to 3
2. 7 to 10
3. 25 to 30
4. 50 to 100
strength of nylon
width is
91. Knitted fabric width is expressed as
1. Total number of needles x wales per
inch
2. Total number of needles wales per
inch
3. Total number of needles - wales per
inch
87. The number of twistslmetre involved in high
stretch yarns is around
1. 100
2. 2500
3. 500
4. 250
88. An unbalanced structure in weft knitting
process is
1. Polka rib
2. Royal rib
3. Eight lock
4. Derby rib
89. In Jacquard knitting the maximum design
width of intermediate Jacquard is
1. 48 wales
2. 24 wales
3. 144 wales
4. 182 wales
4. Wales per inch Total no. of needles
92. According to law which of the
following relations is correct in weft knitting?
where S = Stitch density
is constant
= Stitch length
93. In purl knitting machine the two needle beds
are set a t
1.
2.
3.
90. The normal cut of the
non-Jacquard knitting
machine is around
1. 24
2. 48
3. 72
4. 88
-
320
94.
-320From tricot knitting machine the fabric
comes off the machine a t an angle of
2.
3.
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
4.
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
95. The width of Raschel machines varies from
1. 480 to 600 cm
2. 200 to 350 cm
3. to 1500 cm
150 t o 200 cm
96. In the dielectric phenomenon of fibres water
is considered to be
1. Induced dipole
2. Permanent dipole
3. Temporary dipole
4. An ordinary molecule
97. The percentage amorphous region in wool
fibre is around
98. Higher the bi-refringence of a fibre
1. higher will be the orientation
2. lower will be the orientation
3. higher will be the amorphous portions
4. higher will be the crystallinity
99. The optical orientation factor of an isotropic
fibre is
101. The best synthetic fibre for good elastic
recovery is
1. Polyester
2. Nylon
3. Acrylic
4. Polypropylene
102. The % absorption moisture regain of nylon
6.6 at 65% R.H. and 20C is
1. 4.1
2. 2.1
3. 8.0
4. 0.4
103. The chemical potential of a solute in an ideal
solution may be expressed as
104. The reactive dyeing process for 100 % cotton
garment involves duration of dyeing as
1. 1 to 2 hours
2. 2 to hours
3. 3 to 4 hours
4. 5 to 6 hours
105. The interfibrillary swelling takes place in
1. water solution
acid and strong alkali solution
3. water and weak alkali solution
4. alkali solution
100. With increase in relative humidity, the
106. The heat of for cotton fibre is
strength of wool fibre
1. increases
2. decreases
3. first increases and then decreases
4. does not change
1. 17.9
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
107. The simple test for mercerization of cotton is
1. Examining under sunlight
2. Examining under U.V. light
3. Examining through microscope
4. Examining through infra-red light
108. The cross-section of cotton fibre changes due
111. The top roller of two bowl calender used for
calendering process is made of
1. hard plastic
2. hard steel
3. soft paper
4. wood
112. Which one of the following fibres is not used
to mercerization from
1. Flat shape to oval shape
2. Bean shape to round shape
3. Round shape to elliptical shape
4. Elliptical shape to bean shape
for the production of
1. Viscose rayon
2. Glass
3. Polyester
4. Silk
cord?
109. The removal of sericine results in a weight
113. The stelometer is made of CRL system by
1. step synchronous motor
loss of silk by 2. damping device
1. 40 to 75 %
2. 70 to 90 %
3. 2 0 t o 2 5 %
110. The california bearing ratio resistance in
textiles is expressed as
1. CBR resistance = failure load crosssectional
area
2. CBR resistance = cross-sectional area
3. cam drive
4. beam design
114. For 3 % trash in mixing the cleaning
efficiency expected in is
1. 65 %
2. 35 %
3. 80 %
4. 25 %
I n single yarn tensile strength test, higher
failure load
1. lower the strength
will result
3. CBR resistance = failure load x crosssectional
area
4. CBR resistance = cross-sectional area -
failure load
2. no change in strength
'3. higher the strength
4. no change in extension
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
Reply With Quote
  #6  
15th January 2014, 09:35 PM
jpnbiswal
Junior Member
 
Join Date: Dec 2013
Posts: 9
Default Re: Study material for textile engineering service? Previous years solved question papers?

PART 10 - TEXTILE TECHNOLOGY
(Answer ALL questions)
76. The tensile strength of polynosic fibre is
around
1. 3 to 3.5 gmsldenier
3. to gmsldenier
77. In viscose solution preparation xanthation
process takes normally from
1. 10 minutes
60 to 180 minutes
3. 5 hours
4. 24 hours
78. The temperature of molten polymer in nylon
81.
82.
The tenacity range of acrylic fibre in
gmsldenier is
1. to 1.2
The modern false twist texturizing machines
can impart false twist in to moving yarn a t
the rate of
1. six million RPM
2. 1 2 million RPM
3. only 30,000 RPM
4. RPM only
66 manufacture is around
79. In acrylic fibre manufacture, the polymer
concentration ranges from
83. High bulk yarns are produced from
1. relaxed fibres
2. unrelaxed fibres
3. a blend of relaxed and unrelaxed fibres
filaments
84. The cord fabrics used in conveying belt
applications approximately weigh
4. 70 to 8 0 %
80. The work factor of viscose staple fibre is
around
85. The cotton cloth construction normally
applied in V-belts in and
is
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
86. The standard
parachute cloth in
1. 2 to 3
2. 7 to 10
3. 25 to 30
4. 50 to 100
strength of nylon
width is
91. Knitted fabric width is expressed as
1. Total number of needles x wales per
inch
2. Total number of needles wales per
inch
3. Total number of needles - wales per
inch
87. The number of twistslmetre involved in high
stretch yarns is around
1. 100
2. 2500
3. 500
4. 250
88. An unbalanced structure in weft knitting
process is
1. Polka rib
2. Royal rib
3. Eight lock
4. Derby rib
89. In Jacquard knitting the maximum design
width of intermediate Jacquard is
1. 48 wales
2. 24 wales
3. 144 wales
4. 182 wales
4. Wales per inch Total no. of needles
92. According to law which of the
following relations is correct in weft knitting?
where S = Stitch density
is constant
= Stitch length
93. In purl knitting machine the two needle beds
are set a t
1.
2.
3.
90. The normal cut of the
non-Jacquard knitting
machine is around
1. 24
2. 48
3. 72
4. 88
-
320
94.
-320From tricot knitting machine the fabric
comes off the machine a t an angle of
2.
3.
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
4.
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
95. The width of Raschel machines varies from
1. 480 to 600 cm
2. 200 to 350 cm
3. to 1500 cm
150 t o 200 cm
96. In the dielectric phenomenon of fibres water
is considered to be
1. Induced dipole
2. Permanent dipole
3. Temporary dipole
4. An ordinary molecule
97. The percentage amorphous region in wool
fibre is around
98. Higher the bi-refringence of a fibre
1. higher will be the orientation
2. lower will be the orientation
3. higher will be the amorphous portions
4. higher will be the crystallinity
99. The optical orientation factor of an isotropic
fibre is
101. The best synthetic fibre for good elastic
recovery is
1. Polyester
2. Nylon
3. Acrylic
4. Polypropylene
102. The % absorption moisture regain of nylon
6.6 at 65% R.H. and 20C is
1. 4.1
2. 2.1
3. 8.0
4. 0.4
103. The chemical potential of a solute in an ideal
solution may be expressed as
104. The reactive dyeing process for 100 % cotton
garment involves duration of dyeing as
1. 1 to 2 hours
2. 2 to hours
3. 3 to 4 hours
4. 5 to 6 hours
105. The interfibrillary swelling takes place in
1. water solution
acid and strong alkali solution
3. water and weak alkali solution
4. alkali solution
100. With increase in relative humidity, the
106. The heat of for cotton fibre is
strength of wool fibre
1. increases
2. decreases
3. first increases and then decreases
4. does not change
1. 17.9
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
107. The simple test for mercerization of cotton is
1. Examining under sunlight
2. Examining under U.V. light
3. Examining through microscope
4. Examining through infra-red light
108. The cross-section of cotton fibre changes due
111. The top roller of two bowl calender used for
calendering process is made of
1. hard plastic
2. hard steel
3. soft paper
4. wood
112. Which one of the following fibres is not used
to mercerization from
1. Flat shape to oval shape
2. Bean shape to round shape
3. Round shape to elliptical shape
4. Elliptical shape to bean shape
for the production of
1. Viscose rayon
2. Glass
3. Polyester
4. Silk
cord?
109. The removal of sericine results in a weight
113. The stelometer is made of CRL system by
1. step synchronous motor
loss of silk by 2. damping device
1. 40 to 75 %
2. 70 to 90 %
3. 2 0 t o 2 5 %
110. The california bearing ratio resistance in
textiles is expressed as
1. CBR resistance = failure load crosssectional
area
2. CBR resistance = cross-sectional area
3. cam drive
4. beam design
114. For 3 % trash in mixing the cleaning
efficiency expected in is
1. 65 %
2. 35 %
3. 80 %
4. 25 %
I n single yarn tensile strength test, higher
failure load
1. lower the strength
will result
3. CBR resistance = failure load x crosssectional
area
4. CBR resistance = cross-sectional area -
failure load
2. no change in strength
'3. higher the strength
4. no change in extension
____________Download From www.JbigDeaL.com Powered By JbigDeaL____________
Reply With Quote
  #7  
9th April 2014, 02:44 PM
Unregistered
Guest
 
Posts: n/a
Default Re: Study material for textile engineering service? Previous years solved question papers?

Sir pls tell me the book for combined engineering service electrical and model question too this s mail is [email protected]
Reply With Quote
  #8  
6th May 2014, 04:38 PM
Unregistered
Guest
 
Posts: n/a
Default Re: Study material for textile engineering service? Previous years solved question papers?

dear sir please send q&a for textile engineering

Regards,
gkr.prakash 9884055814
anybodies send me [email protected]
Reply With Quote
  #9  
17th July 2018, 01:46 PM
Unregistered
Guest
 
Posts: n/a
Default Re: Study material for textile engineering service? Previous years solved question papers?

Sir please send the textile Engineering Solve Question Paper from 2005 to 2010
Reply With Quote
Do you have any question? or have anything to say?



Related Topics:

Thread Replies Last Post
Combined Engineering Services exam study material 75 10th January 2018 10:38 PM
TNPSC combined engineering service examination (civil engineering) question paper 29 31st July 2015 11:13 AM
Previous question paper for TNPSC AE post in civil engineering, TNPSC combined engineering service exam 37 31st March 2014 01:12 PM
Textile Engineering objective type question papers (solved) and study material 24 15th January 2014 09:33 PM
Past 5 years question papers with answers for combined engineering service for post of AE Civil Engineering? 1 3rd October 2011 10:06 AM



Powered by vBulletin® Version 3.8.3
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
Search Engine Optimization by vBSEO 3.3.0
vBulletin Optimisation by vB Optimise.
Please also check: